Plastic compositions

ABSTRACT

Plastic compositions containing a three component system consisting of (1) polycarbonate, (2) certain bis-phenoxy compounds having the formula: ##STR1## WHEREIN Z is bromine, m and m&#39; are each integers having a value of 1-5 with the proviso that the total bromine atom content is from 6 to 10, and &#34;T&#34; is a straight or branched chain carbon group having 1 to 4 carbon atoms, and (3) an enhancing agent, hereinafter defined.

RELATED PATENT APPLICATIONS

This application is a continuation-in-part of a copending application Ser. No. 330,841, filed Feb. 8, 1973. The entire specification of Ser. No. 330,841, is to be considered as incorporated herein by reference.

PRIOR ART

The prior art considered in conjunction with the preparation of this application is as follows: U.S. Pat. No. 1,979,145; U.S. Pat. No. 2,130,990; U.S. Pat. No. 2,186,367; U.S. Pat. No. 2,263,444; U.S. Pat. No. 2,329,033; U.S. Pat. No. 2,488,499; U.S. Pat. No. 2,738,351; U.S. Pat. No. 2,797,246; U.S. Pat. No. 2,930,815; U.S. Pat. No. 3,385,819; U.S. Pat. No. 3,549,591; U.S. Pat. No. 3,560,441; U.S. Pat. No. 3,649,591; U.S. Pat. No. 3,658,634; U.S. Pat. No. 3,666,692; U.S. Pat. No. 3,686,320; U.S. Pat. No. 3,697,456; U.S. Pat. No. 3,717,609; U.S. Pat. No. 3,763,243; U.S. Pat. No. 3,787,506; German Pat. No. 891,549; German Pat. No. 1,139,636; German Pat. No. 2,054,522; Japanese Pat. No. (72) 14,500 (and as cited in Volume 77, Chemical Abstracts, column 153737k, 1972); Chemical Abstracts, Volume 13, column 448⁵ ; Chemical Abstracts, Volume 31, column 7045.sup. 9 ; Chemical Abstracts, Volume 52 (1958), column 4543-4544; Journal of the Chemical Society, pages 2972-2976 (1963); Journal of the American Chemical Society, Volume 57 (1935), pages 572-574 and Volume 76 (1954), page 2993; Journal of the Science of Food and Agriculture, Volume 20 (1969), pages 748-754; Philippine Journal of Science, Volume 34 (1927), page 159; and Japanese Patent publication 022, 456 of 1974.

All of these publications are to be considered as incorporated herein by reference.

BACKGROUND OF THE INVENTION

The present invention relates to plastic compositions containing a polycarbonate. More specifically, the present invention covers plastic compositions containing a three component system which consists of polycarbonate, certain bis-phenoxy compounds (hereinafter defined) as flame retardants for said plastic compositions, and an enhancing agent (hereinafter defined) for said flame retardants.

Polycarbonates and utility thereof are known in the art as exemplified by Polycarbonates, W. F. Christopher and D. W. Fox, (Reinhold Plastics Applications Series), Reinhold Publishing Corporation, New York, 1964 and Modern Plastics Encyclopedia 1972-1973, Vol. 49: No. 10A, October, 1972, pages 72, 155, 156 and 215-217 and which publications are in toto incorporated herein by reference.

The need for flame retarding polycarbonates has also been recognized in the art as exemplified by U.S. Pat. No. 3,422,048 and Modern Plastics Encyclopedia, ibid, pages 155, 156 and 456-458 and which publications are in toto incorporated herein by reference.

The prior art has specifically recognized the problems of finding suitable flame retardants for polycarbonates in view of the fact that polymer systems differ substantially in both flammability characteristics and physical properties and there is no predictability whatsoever from one system to another. Thus in the Norris et al paper entitled "Toxicological and Environmental Factors Involved in the Selection of Decabromodiphenyl Oxide as a Fire Retardant Chemical", Applied Polymer Symposium No. 22, 195-219 (1973), the authors state: "A growing recognition of the huge annual toll taken by fire is resulting in more stringent flammability requirements for synthetic polymers in a variety of applications. Because of economic constraints and the need to produce flame resistant polymers without total replacement of existing manufacturing processes, increased flame resistance is generally achieved by incorporation of a fire retardant chemical in the finished product. This chemical is usually based on bromine, chlorine, phosphorus, or nitrogen and may either be chemically reacted or physically blended into the product. Since polymer systems differ markedly in both flammability characteristics and physical properties, selection of a suitable flame retardant depends on a variety of factors that severely limits the number of acceptable materials.

"A general class of synthetic polymers that require flame retardancy because of their use in electrical and high temperature applications, but pose severe problems in selecting a suitable flame retardant are the high performance thermoplastic resins such as thermoplastic polyesters, polyphenylene oxides, and acrylonitrile-butadiene-styrene (ABS) terpolymers. Some of the most important criteria for an acceptable flame retardant in these applications are:

1. It must be as effective as possible to minimize both cost and effect on polymer properties. Use levels may range up to 15% by weight.

2. It must have sufficient stability to withstand conditions encountered during polymer processing and use. Processing conditions (blending, extrusion, and molding) often involve temperatures exceeding 300° C. The flame retardant must tolerate these conditions without degradation or volatilazation. Also, attention must be given to hydrolytic stability and oxidative degradation, particularly under extended service at high temperatures.

3. It must be compatible with the base polymer and exert minimal adverse effect on those properties that give the polymer its value. Some of these critical properties are tensile strength, impact strength, heat deflection temperature, shear strength, and flexural modulus.

4. Finally, the flame retardant must not interfere with attainment of desired product esthetics and form.

"Because of the stringest thermal stability requirements, only a very few compounds have been identified which can meet the necessary performance and economic criteria."

The resultant disadvantages in the utilization of various prior art materials as flame retardants, in general, for plastic compositions include, without limitation, factors such as thermal migration, heat instability, light instability, non-biodegradable, toxicity, discoloration, the large amounts employed in order to be effective, and the unpredictable and results obtained when using the same material in different plastics (note, for example, in Modern Plastics Encyclopedia, ibid, page 650, wherein octabromobiphenyl is suitable for use in polyolefins as a flame retardant therefor, but is not shown for use (or functionally equivalent) as such for the other 27 compositions listed such as ABS, polycarbonates, polystyrene, acrylics and polyurethanes). Thus, it can be seen that the field of flame retardancy is highly sophisticated and consequently requires substantial research effort to achieve a particular desired end result.

In conjunction with the rendition of a polycarbonate flame retardant the aforegoing discussion is particularly applicable. Furthermore, it is desirable that, in addition to the retention of good physical characteristics, three characteristics (one of which is critical) of the product polycarbonate be within certain defined limitations in order to provide a functional flame retarded product. These three characteristics are (1) light stability (as measured, for example, by Δ E color values, hereinafter defined), (2) flame retardancy (as measured, for example, by UL 94, hereinafter defined, and which is a critical characteristic and limitation), and (3) thermal stability (as measured, for example, by certain ASTM tests for decomposition and migration, hereinafter defined). This characteristic of flame retardancy is not an arbitrary item but is a criteria which is strictly adhered to in the polycarbonate art and hereinafter explained in more detail, with particular reference to the examples contained herein.

In conjunction with the foregoing discussion, the prior art in general suggests the use of halogen-containing materials as "potential" or "possible" flame retardants for plastic materials. However, the prior art also recognizes that any material must be adjudged on a case by case basis because of the unpredictable results of the end product when any additive is incorporated therein. For example, with reference to the use of a halogenated fire retardant in U.S. Pat. No. 3,658,634 attention is directed to the fact that the patentee specifically points out the disadvantages in the use of a halogen-containing fire retardant. In Column 1, lines 14-17, the patentee states: "Therefore, if it is possible to impart fire-retardancy to the thermoplastic polymers without deteriorating the useful properties of the thermoplastic polymers, they can be widely used in the field of inertia, construction and electric industries." In Column 1, lines 26-32 the patentee states: "--the compounds containing chlorine or bromine atoms to be used as fire-retardant agents, are generally sublimated and therefore, the fire retardant agents are sublimated and lost in the process for producing fire-retardant polymers or in after-finishing processes; accordingly, deteriorations of fire-retardancy or difficulties in use tend to occur more often than not."

In Column 1, lines 39-44 the patentee states: "--the compounds containing chlorine or bromine atoms to be used as fire-retardant agents are unstable in most cases when exposed to ultraviolet rays." In Column 1, lines 59-64 the patentee states: "However, as a matter of fact, only very few fire-retardant polymers can be used in actual practice although they are said to have fire-retardant effects, because there are restrictions such as the conditions employed in production attributable to the properties of the fire-retardant agent, or to the properties of the polymers into which they are to be incorporated."

It can be seen, then, from the foregoing discussion and quoted subject matter that the field of flame retardancy is highly sophisticated, unpredictable and requires substantial research to produce an end product (plastic composition) which meets the necessary criteria for utilitarian purposes, particularly under the present day government standards. Thus, there is always a demand for a material which will function as a flame retardant in a polycarbonate and concurrently will not, by incorporation therein, adversely effect the chemical and/or physical and/or mechanical properties of the resultant polycarbonate containing plastic composition (herein also referred to as "polycarbonate plastic composition") and also have utility.

The prior art problem of providing a flame retarded polycarbonate composition having desired chemical, physical and mechanical properties, in addition to functional utility, has now been substantially solved by the present invention and the above-described disadvantages substantially overcome.

Accordingly, one of the main objects of the present invention is to provide polycarbonate plastic compositions which are flame retarded.

Another object of the present invention is to provide a unique three component system for polycarbonate plastic compositions which will not substantially adversely effect the chemical and/or physical and/or mechanical properties of said compositions.

A salient object of the present invention is to provide a polycarbonate plastic composition which has a certain defined flame retardancy property.

A further object of the present invention is to provide a flame retardant and an enhancing agent which are economical and easy to incorporate into polycarbonates without being degraded or decomposed as a result of normal blending or processing operations.

BRIEF DESCRIPTION OF THE INVENTION

It has been found that the foregoing objects can be obtained by the use of a unique three component system, which consists of (a) a polycarbonate (hereinafter defined), (b) certain bis-phenoxy compounds (hereinafter defined), and (c) an enhancing agent (hereinafter defined) to subsequently provide flame retarded plastic compositions which exhibit outstanding chemical, physical and mechanical properties.

It is to be understood that the term "flame retarded" as used herein refers and is restricted to a limited definition and that is the reduction in flammability of the plastic composition which contains the three component system. The criticality of this flame retardancy is more specifically set forth herein, with particular reference being made to page 19 herein regarding UL 94 classification (sometimes referred to herein as "values").

DETAILED DESCRIPTION OF THE INVENTION

The particular class of bis-phenoxy compounds used in the present invention compositions have the formula ##STR2##

In Formula I above, Z is bromine, m and m' are each an integer having a value of 1 to 5 inclusive with the proviso that the total bromine content of said compound is six (6) to ten (10) bromine atoms inclusive, and T is (1) a straight chain carbon group having from one to four carbon atoms and includes, without limitation, groups such as --CH₂ --; --(CH₂)₂ --; --(CH₂)₃ --; and --(CH₂)₄ --; and (2) a branched chain carbon group having from two to four carbon atoms and includes, without limitation, groups such as follows: ##STR3## and ##STR4##

It is to be understood that all the compounds falling within Formula I above and as heretofore defined are generically described herein as "bis-phenoxy" compounds.

Representative, but without limitation, of said bisphenoxy compounds are the following: ##STR5## 1,2-bis(2,4,6-tribromophenoxy) ethane ##STR6## 1,3-bis(2,4,6-tribromophenoxy) propane ##STR7## 1,4-bis(2,4,6-tribromophenoxy) butane ##STR8## 2,2-bis(2,3,4,5-tetrabromophenoxy) propane ##STR9## 1,2-bis(2,3,4,5,6-pentabromophenoxy) ethane ##STR10## 1,1-bis(2,3,4,5,6-pentabromophenoxy) methane ##STR11## 1,1-bis(2,4,6-tribromophenoxy) methane ##STR12## 1-(2,3,4,5,6-pentabromophenoxy), 2-(2,4,6-tribromophenoxy) ethane

In general, the bis-phenoxy compounds are prepared by reacting a halogenated phenol with a halogenated alkane at elevated temperatures in the presence of a basic material such as alkali metal hydroxides, carbonates, bicarbonates, oxides and hydrides. The preferred alkali metals are potassium and sodium. Where one desires to increase, for example, ease of handling the reaction mass, solvents such as ketones (e.g. acetone, methyl ethyl ketone, and methyl iso-butyl ketone), alcohols (e.g. methanol, ethanol, iso-propyl alcohol, butyl alcohol and glycols), or aqueous solvents (e.g. water, a mixture of water and alcohol and a mixture of water and ketone) can be employed. The desired end product i.e. the bis-phenoxy compound, can be recovered from the reaction mass via various methods known to those skilled in the art. Where the end product requires recovery via crystallization, various aromatic solvents, such as benzene, toluene, xylene, dichlorobenzene and the like, can be used.

Specifically, the bis-phenoxy compounds are prepared according to the following reactions: ##STR13##

In the above reaction, X is halogen, preferably bromine, and T is the same as herein defined.

The above reaction is conducted at temperatures ranging from the freezing point of the initial reaction mass to the boiling point hereof. Preferably the temperatures are from about 40° C. to about 200° C. and more preferably from about 50° C. to about 175° C. It is to be understood that the reaction can be conducted under sub-atmospheric (e.g. 1/10-8/10 atmospheres) pressure. Preferably, the reaction is carried out at atmospheric pressure.

The above-described processes can be carried out with conventional, readily available chemical processing equipment. For example, a conventional glass-lined vessel provided with heat transfer means, a reflux condenser and a mechanical stirrer can be advantageously utilized in practicing any of the preferred embodiments of the invention described in preparing the bis-phenoxy examples set forth herein.

The amount of bis-phenoxy compound employed in the present invention compositions is any quantity which will effectively render, in conjunction with the enhancing agent, the polycarbonate containing composition flame retardant. In general, the amount used is from about 1% to 25% by weight, based on the total weight of the composition. Preferably, the amount employed is from about 1% to about 10% by weight. It is to be understood that any amount can be used as long as it does not substantially adversely effect the chemical and/or physical and/or mechanical properties of the end plastic composition. The amount utilized, however, is such amount which achieves the objectives described herein.

The second component of the three component system, and which is critical therefor, are certain compounds which when used with the bis-phenoxy compounds promote a cooperative effect therebetween and thus enhance the flame retardancy of the resultant plastic composition as compared to the flame retardancy of either one component used separately. These "enhancing agents" comprise the oxides and halides of groups IVA and VA of the Periodic Table, i.e. oxides and halides of antimony, bismuth, arsenic, tin, lead, germanium, e.g. antimony oxychloride, antimony chloride, antimony oxide, stannic oxide, stannic chloride, arsenous oxide, arsenous chloride, and the like; and organic and inorganic compounds of phosphorus, nitrogen, boron, and sulfur, e.g., triphenyl phosphate, ammonium phosphate, zinc borate, thiourea, urea, stannic sulfide, and the like and oxides and halides of titanium, vanadium, chromium, manganese, iron, niobium, molybdenum copper, zinc, magnesium, e.g., titanium dioxide, titanium chloride, vandanium pentoxide, chromic bromide, manganous oxide, molybdenum trioxide, ammonium molybdate; and hydrates of the above, e.g., stannic oxide hydrate, lead hydrate; and combinations thereof. The preferred enhancing agents are the oxides of antimony, arsenic and bismuth. However, any compound which on decomposition, as by ignition, yields these oxides would be suitable. Thus some organic antimonates are preferred. The enhancing agents disclosed in U.S. Pat. No. 3,205,196 are also suitable for use.

U.S. Pat. No. 3,205,196, column 2, states that "Antimony oxide is the antimony compound that is presently preferred for use in the present invention. However, many antimony compounds are suitable, inorganic antimony compounds include antimony sulfide sodium antimonite, potassium antimonite, and the like. Many organic antimony compounds are suitable such as the antimony salts of organic acids and their pentavalent derivatives disclosed in copending application Ser. No. 688,143, filed Oct. 4, 1957, now U.S. Pat. No. 2,996,528. Compounds of this class include antimony butyrate, antimony valerate, antimony caproate, antimony heptylate, antimony caprylate, antimony pelargonate, antimony caprate, antimony cinnamate, antimony anisate, and their pentavalent dihalide derivatives. Likewise the esters of antimonous acids and their pentavalent derivatives disclosed in copending application Ser. No. 688,108, filed Oct. 4, 1957, now U.S. Pat. No. 2,993,924, such as tris(n-octyl) antimonite, tris(2-ethylhexyl) antimonite, tribenzyl antimonite, tris(β-chloroethyl) antimonite, tris(β-chloropropyl) antimonite, tris(β-chlorobutyl) antimonite and their pentavalent compounds are the cyclic antimonites such as trimethylolpropane antimonite, pentaerythritol antimonite, and glycerol antimonite. The corresponding arsenic and bismuth compounds can also be employed."

It is to be understood that such patents as U.S. Pat. No. 3,205,196; U.S. Pat. No. 2,996,528 and U.S. Pat. No. 2,993,924 are to be considered as incorporated herein by reference for all intents and purposes. Without limitation, preferred enhancing agents include Sb₂ O₃, SbCl₃, SbBr₃, SbI₃, SbOCl, As₂ O₃, As₂ O₅, ZnBO₄, BaB₂ O₄ .H₂ O, 2.ZnO. 3B₂ O₃. 3.5H₂ O and stannic oxide hydrate. The more preferred enhancing agent is antimony trioxide.

The amount of enhancing agent employed in the present invention compositions is any amount which when used with said bisphenoxy compounds will promote a cooperative effect therebetween. In general, the amount employed is from about 0.5% to about 15%, preferably from about 1% to about 10%, by weight, based on the total weight of plastic composition. Higher or lower amounts can be used as long as the desired end result is achieved.

The third critical component of the three component system is the polycarbonate. It is to be understood that the term "polycarbonate(s)" as used herein means linear thermoplastic polyesters of carbonic acid with aliphatic or aromatic dihydroxy compounds. They may be represented by the following formula: ##STR14## where R is generally aromatic This term includes copolycarbonates (from aromatic or aliphatic dihydroxy compounds) and copoly(ester-carbonates) and poly(carbonate-urethanes).

Thus the polycarbonate used in the present invention compositions is any polycarbonate herein defined and which one so desires to flame retard. It is to be understood that the polycarbonate used can be a "virgin" material, i.e. substantially free of additives such as stabilizers, plasticizers, dyes, pigments, fillers, and the like, or the polycarbonate can have additives (such as those mentioned and described herein) already contained therein or added concurrently with or after the addition of the bis-phenoxy compounds and enhancing agents.

It is to be understood that the term "polycarbonate", as used herein, includes, without limitation, those polycarbonates which are also more fully described in Encyclopedia of Polymer Science and Technology, Volume 10, pages 710-715 (1969). The preferred type of polycarbonate polymers is based on the utilization of bisphenol A in conjunction with the preparation of said polymers.

The bis-phenoxy compounds and enhancing agents can be incorporated into the polycarbonate at any processing stage in order to prepare the present invention plastic compositions. In general, this is undertaken prior to fabrication either by physical blending or during the process of forming the polycarbonate per se. Where one so desires, the bis-phenoxy compounds and/or enhancing agents may be micronized into finely divided particles prior to incorporation into the polycarbonate.

It is also within the scope of the present invention to employ other materials in the present invention compositions where one so desires to achieve a particular end result. Such materials include, without limitation, adhesion promotors; antioxidants; antistatic agents; antimicrobials; colorants; flame retardants such as those listed on pages 456-458, Modern Plastics Encyclopedia, ibid., (in addition to the new class of flame retardants described herein); heat stabilizers; light stabilizers; pigments; plasticizers; preservatives; ultraviolet stabilizers and fillers.

In this latter category, i.e. fillers, there can be mentioned without limitation, materials such as glass; carbon; cellulosic fillers (wood flour, cork and shell flour); calcium carbonate (chalk, limestone, and precipitated calcium carbonate); metal flakes; metallic oxides (aluminum, beryllium oxide and magnesia); metallic powders (aluminum, bronze, lead, stainless steel and zinc); polymers (comminuted polymers and elastomerplastic blends); silica products (diatomaceous earth, novaculite, quartz, sand, tripoli, fumed colloidal silica, silica aerogel, wet process silica); silicates (asbestos, kaolimite, mica, nepheline syenite, talc, wollastonite, aluminum silicate and calcium silicate); and inorganic compounds such as barium ferrite, barium sulfate, molybdenum disulfide and silicon carbide.

The above mentioned materials, including filler, are more fully described in Modern Plastics Encyclopedia, ibid, and which publication is incorporated herein (in toto) by reference.

The amount of the above described materials employed in the present invention compositions can be any quantity which will not substantially adversely effect the desired results derived from the present invention compositions. Thus, the amount used can be zero (0) percent, based on the total weight of the composition, up to that percent at which the composition can still be classified as a plastic. In general, such amount will be from about 0% to about 75% and more specifically from about 1% to about 50%.

With reference to the present invention plastic compositions described herein, one of the critical features thereof is the unusually high flame retardancy thereof. The significance of flame retardancy of plastic compositions is well recognized in the art as heretofor mentioned. However, recent developments in conjunction with the use of flame retardant plastic compositions as judged by the Consumer Product Safety Commission, require a UL-94 value (hereinafter discussed) of V-0 in order to produce a V-0 acceptable article of manufacture. The Consumer Product Safety Commission is continuing to set mandatory standards in the field where the plastic compositions are utilized and since about 1970 have increased the criticality of the UL value of plastic compositions. In reacting to the Consumer Product Safety Commission's mandatory standards in this area, the producers of (plastic composition) articles of manufacture are now requiring that said articles have a V-0 value in order to meet new mandatory standards which are anticipated to be activated by federal legislation shortly. Thus, the significance of a plastic composition having a V-0 value is well recognized in the art; note Modern Plastics, Sept. 1974, pages 74-77 and which publication is to be considered as incorporated herein by reference.

In conjunction with the present invention plastic compositions described herein, an important feature thereof is the light stability thereof. The significance of light stability of plastic compositions is recognized in the art, e.g. the publication entitled "The Measurement Of Appearance" by Mr. Richard S. Hunter (Hunter Associates Laboratory, Inc., 9529 Lee Highway, Fairfax, Virginia) 1973. Mr. Hunter has been associated with the efforts of defining appearance and color since the 1930's and was for many years an associate of Gardner who is another authority in this field. The following paragraphs from Mr. Hunter's book are set forth in order to demonstrate this light stability significance.

The Judd-Hunter system "of scales for color difference was based on Judd's uniform chromaticity scales triangle. Judd made an instrumental study of a number of woolen swatches rated by dyers for their acceptability as commercial color matches to standard. The NBS unit of color difference was designed by Judd to be the maximum difference commercially acceptable in the textile trade as represented by these dyers at the time when the study was carried out (Judd, 1939). The NBS Unit generally referred to today is not Judd's 1939 unit, but the Hunter 1942 version of the Judd unit with 100 units falling between black and white."

"Since 1942 this unit has been used in terms of a number of the opponent color scales. In a color scale which is already uniform in its visual spacing of lightness and chromaticity, and which has 100 units between black and white as well as rectangular coordinates for chromaticity, color difference in approximate NBS units can be specified in units of that system. The color difference becomes the distance between the two colors in that color space. With rectangular coordinates, the formula is:

    ΔE=√ΔL.sup.2 +Δa.sup.2 +Δb.sup.2

Similarly if only the chromaticity component of difference is desired, the formula is:

    ΔC=√Δa.sup.2 +Δb.sup.2

"Following Judd's proposed unit of color difference, Hunter proposed the measurement of much the same quantity by a photoelectric tristimulus method in 1942. In the next year, Scofield proposed a quantity which was quite a bit easier to compute. Scofield used the reciprocal of the square root of reflectance instead of the reciprocal of the fourth root of reflectance as a multiplier in adjusting reflectance values for uniform lightness scale intervals. This is the only difference between the Scofield and the Judd-Hunter formulas for color difference. (Scofield, 1943)."

"In 1948, Hunter started to develop a tristimulus instrument which would read chromaticity dimensions of opponent colors directly. He was seeking to improve the precision and usefulness of results of the tristimulus reflectometers previously used. The R_(d) scales developed in the period 1948 and 1950 did not have a uniform lightness readout but did have direct reading visually uniform a and b scales. The L scales, in which there is approximate perceptual uniformity in all three dimensions, were created in the period 1950-1952 but were not described in a formal publication until 1958. These two sets of Hunter Color Difference Meter scales enjoy wide use because of the fact that they can be read directly from a tristimulus instrument with high precision, and offer instrumental computation of color difference by the ΔE formula given above."

"NBS Unit of Color Difference is defined as: the unit of color difference of the National Bureau of Standards. The unit is about four times as great as the smallest difference observable under ideal conditions. Differences of less than one unit are usually not important in commercial transactions. In Munsell terms, one NBS unit is equivalent to about 0.1 Value step, 0.15 Chroma step, or 2.5 Hue step at Chroma 1."

"Hunter further investigated the use of L',α', β' for color difference measurement. He recognized at this time (which no other color-difference scale before or since has recognized) that perceived color difference will depend on the proximity of the specimens compared and on their glossiness. Accordingly, the 1942 Hunter color difference equation includes factors to account for these variables. It is this equation, with selected constants, that defines the widely used NBS unit of color difference."

"High precision is almost always essential for useful color difference measurements. Only with precise instruments is it possible to measure color differences as small as those the eye can see. Instrument accuracy is also normally a requisite because spectrally inaccurate instruments, even though precise, will give visually inaccurate color difference measurements wherever there are spectral differences between the specimens involved. The ease of obtaining and interpreting values of color difference is another factor which may affect the selection of a procedure."

"Twenty years ago, color difference scales were in demand to serve as a basis for setting one-number tolerances for fading and acceptability of matches. The Index of Fading and NBS unit were used as units."

"Today, the concept of color difference is more refined. One number tolerances are seldom used. Instead, color difference tolerances are designed as boundaries in color space within which acceptable colors must fall. The boundaries do not necessarily correlate with perceptibility of difference but rather with the limits of acceptability. The standard color, furthermore, may not be in the center of the bounded region but may be displaced to one side. For example, where subsequent yellowing may occur, the tolerance for the yellow-blue dimension might be +0.1, -0.8 units."

"Color difference specifications are tighter today and tolerances are smaller. The specification usually treats the color dimensions separately so that a complete specification would contain nine numbers: The three numbers that describe the desired color, and the six numbers that describe the individual plus and minus tolerances. Such tolerances can be reduced to graphs which not only show acceptability but provide a guide to the formulation correction needed to correct an off shade. When the question of acceptability becomes a question of sorting objects according to shade, a graphical chart showing the classification of color values can be quite helpful."

"Although color measurements are frequently used for identification, sorting and recording of color values, the primary uses of tristimulus instruments all involve measurements of fairly small color differences. The most frequent uses of these small color difference measurements are to establish closeness to standard and to give guidance for the adjustment of color mismatches. They are also used in the study of deterioration in a product as a result of exposure and use."

"Spectrophotometers and tristimulus instruments made up the majority of color appearance measuring instruments in use in industry. Spectrophotometers give wavelength-by-wavelength analyses of the reflecting properties of objects, while tristimulus instruments by the use of filters which approximate the Standard Observer functions of the eye, give measurements of color in X, Y, Z terms, or in L, a, b values. Spectrophotometers are essential where color formulation is involved, and metamerism must be controlled. However, tristimulus colorimeters and reflectometers provide precise and less expensive means for the routine measurement of color and adjustment of small color differences."

In view of the foregoing quoted subject matter, it can thus be seen that a change in ΔE value of 1 unit constitutes a real change. Note also Japanese patent application (publication 022,456 of 1974) which shows that achieving a color change in ΔE of only 2.3 is significant as it pertains to a polycarbonate polymeric composition; (this value is substantially the same as those ΔE values obtained in polycarbonate tests and which results thereof are shown in Table IV herein, i.e. 2.3 versus 2.5 over the control). Both of these publications (i.e. the Japanese Pat. No. 022,456 and the Hunter book) are to be considered as incorporated herein by reference. It is to be noted also that a lower ΔE value is more desired and the higher ΔE value is least desired. This ΔE value is not an abstract value, however, since one must compare it with the ΔE values of the "control" plastic composition. One of the desired ΔE values would be where both the ΔE values of the "control" plastic composition (without additives-i.e. without flame retardant and enhancing agent) and the plastic composition with said additives are substantially the same or the latter has a lower value. In an polycarbonate composition, a ΔE value of less than 10 is considered desirable for commercial applications.

EXAMPLE I

A virgin polycarbonate plastic material, (Lexan 101, a product of General Electric Company) is utilized as the base resin in order to prepare 9 formulations (plastic compositions). With the exception of formulation No. 1, the particular bis-phenoxy compound (and the antimony trioxide enhancing agent where indicated) is incorporated into the plastic by adding both to a Brabender mixer ("Plastic-Corder", Torque Rheometer, Model PLV-150, C. W. Brabender Instruments, Inc., South Hackensack, N. J.). The mixer is equipped with a pair of roller type blades positioned within a head provided with heat transfer means.

The resultant mixture is heated to about 300° C.; at this temperature, it is in a molten state. The percentages by weight of each component utilized in the respective formulations are listed in Table I. Each formulation is discharged from the mixer and upon cooling solidifies and is ground into chips. The chips are subjected to compression molding in a Wabash press by placing said chips between two platens, the bottom of which contains four equal size depressions three inches by five inches by 1/8 inch deep. The top platen is then placed over the bottom platen and heat transfer means supplied thereto in order to melt said chips and thus provide solid samples (after cooling) for testing.

Portions of the solid samples of each respective formulation (Nos. 1-9) prepared according to the above described procedure are then subjected to two different standard flammability tests, i.e. UL 94 and ASTM D-2863-70. The UL 94 is, in general, the application of a burner to a test specimen (strip) for a certain period of time and observation of combustion, burning and extinguishment. This procedure is fully set forth in Underwriters' Laboratories bulletin entitled UL 94, Standard for Safety, First Edition, Sept., 1972, and which is incorporated herein by reference. ASTM No. D-2863-70 is a flammability test which correlates the flammability of a plastic specimen to the available oxygen in its immediate environment; this correlation is stated as an Oxygen Index, O.I., level predicated upon the percent oxygen in the gaseous medium which is required to just provide a steady state of continuous burning of the plastic specimen. This ASTM method is fully described in 1971 Annual Book of ASTM Standards -- Part 27, published by the American Society for Testing and Materials, 1916 Race Street, Philadelphia, Pa.; this publication is to be considered as incorporated (in toto) herein by reference. The UL 94 test is the more critical test as it is the test generally used to determine the suitability of thermoplastics for commercial applications.

The results of these flammability tests are shown in Table I.

                                      TABLE I                                      __________________________________________________________________________     FLAMMABILITY DATA FOR POLYCARBONATE                                            PLASTIC COMPOSITIONS CONTAINING BIS-PHENOXY COMPOUNDS,                         WITH AND WITHOUT ENHANCING AGENTS                                              FORMULA                                                                               BIS-PHENOXY                                                                            COMPOUND                                                                              ENHANCING AGENT                                                                           OXYGEN                                                                               UL94                                    TION NO.                                                                              FORMULA %      Sb.sub.2 O.sub.3, %                                                                       INDEX %                                                                              VALUE                                   __________________________________________________________________________     1.     --      0      0          25.5  SB                                      2.     III     2      0          30.5  SE-2                                    3.     III     2      2          39.5  SE-0                                    4.     III     4      2          40.0  SE-0                                    5.     III     5      3          >40.0 SE-0                                    6.     III     13     3          >36.0 SE-0                                    7.     II      2      0          29.0  SE-2                                    8.     II      5      3          >40.0 SE-O                                    9.     II      10     3          >40.0 SE-0                                    __________________________________________________________________________

Referring to Table I, the bis-phenoxy compound formula II or III relates to the structural formulae heretofor set forth; and the UL 94 values are on a graduated scale wherein the highest degree to lowest degree of flame retardancy is respectively SE-0, SE-1, SE-2, SB and Burns.

The results shown in Table I demonstrate the unique effectiveness of the plastic composition containing a polycarbonate, the bis-phenoxy compound, and the enhancing agent. Specifically, formulation No. 1 (the control) had a O.I. of 25.5 and UL 94 value of SB. In Nos. 2 and 7, the use of only the bis-phenoxy compound results in no substantial increase in fire retardancy as measured by UL 94; formulation No. 1 had a SB rating, UL 94, and the individual U.L. ratings of formulation Nos. 2 and 7 are SE-2.

The use of the three component system, i.e. the polycarbonate, bis-phenoxy compound and enhancing agent is fully demonstrated via the results obtained from testing formulation Nos. 3-6, 8 and 9. Thus, the use of an enhancing agent such as Sb₂ O₃ to promote a cooperative effect between such agent and the bis-phenoxy compound is quite apparent particularly when viewing the results obtained from testing formulation Nos. 1, 2 and 7. The highest UL 94 ratings are obtained in all cases with the three component system.

EXAMPLE II

The procedure of Example I is repeated except that the bis-phenoxy compound used corresponds to Formula IV, heretofor set forth, instead of Formulae II and III. Substantially the same results are obtained using the Formula IV compound as those obtained using Formulae II and III compounds.

EXAMPLE III

The procedure of Examples I and II are repeated except that the enhancing agent used is zinc borate instead of Sb₂ O₃. Substantially the same results are obtained using zinc borate as those obtained using Sb₂ O₃.

EXAMPLE IV

Strip samples of each of Formulation Nos. 1 (control), 3 and 8, Table I, are subjected to light stability tests via the use of a "Weather-Ometer", model 25/18 W.R., Atlas Electrical Devices Company, Chicago, Illinois. Utilizing an operating temperature of 145° F. and a 50% relative humidity, each strip is subjected to 200 hours of "simulated daylight" via the use of a carbon arc. The results show that after 200 hours, there is no significant discoloration in any strip tested and which demonstrates that the present invention compositions are highly resistant to deterioration by light.

EXAMPLE V

Samples of each of Formulation Nos. 1 (control), 3 and 8, Table I, are subjected to temperature (thermal) stability tests via the use of thermal gravimetric analysis (TGA). This test employed the use of a "Thermal Balance", model TGS-1, Perkin-Elmer Corporation, Norwalk, Connecticut, and an electrical balance, Cahn 2580 model, Cahn Instrument Company, Paramount, California. The results of these tests show that the polycarbonate, bis-phenoxy compound, enhancing agent--containing Formulations had more than adequate stability for melt processing and subsequent heat aging (i.e. high temperature applications) and thus demonstrating that the particular bis-phenoxy/enhancing agent combinations are quite compatible with the polycarbonate material. The bis-phenoxy compound stability thus aids in providing sufficient flame retardancy at the polycarbonate decomposition temperature. This test also demonstrates that the bis-phenoxy compounds do not exhibit migration.

EXAMPLE VI

Examples I - V are repeated with the exception that the base resin used is G.E.'s Lexan 141 polycarbonate plastic material instead of Lexan 101. The same outstanding and unexpected results are obtained using this polycarbonate material as those results obtained from using Lexan 101.

COMPARATIVE EXAMPLES

The following examples are presented to demonstrate the uniqueness of the present invention compositions as contrasted to other plastic compositions containing the same bis-phenoxy compounds, with or without an enhancing agent. These examples also show unpredictability, via the end results, in using the same materials in several different plastics.

Referring more specifically to the following examples, Example VII compares a three component system, i.e. ABS, certain "bis-phenoxy compounds" (herein referred to as BPC) and enhancing agent with four other polymers containing the same bis-phenoxy compounds (as used in the present invention) and enhancing agent. The four comparative polymers are polyacrylonitrile, polypropylene, nylon and polymethylmethacrylate. As will be seen from the results hereinafter set forth, the four other polymers had no flame retardant efficacy when incorporating the bis-phenoxy compounds and enhancing agents, whereas the ABS system did and so demonstrated an unexpected and substantial flame retardant efficacy. These results, thus, are another indication of the unpredictability of additives when incorporated into polymer systems and correspond to the subject matter set forth in "Modern Plastic Encyclopedia", ibid, regarding the use of octabromobiphenyl in one polymer but not shown for use (or functionally equivalent) in numerous other materials.

Referring to Example VIII this example sets forth the comparison of the polycarbonate with seven other polymer systems but in substantially more detail with particular reference to light stability, flammability and thermal stability. The results disclosed in this Example VIII are similar to those results obtained in Example VII.

EXAMPLE VII

Regarding Formulations Nos. 1-10 in Table III, a virgin polyacrylonitrile plastic material, (T-61 polymer crumb, a product of American Cyanamid and characterized as a copolymer of 93% by weight acrylonitrile and about 7% by weight methyl methacrylate) is utilized as the base resin in order to prepare 10 formulations (plastic compositions). With the exception of formulation No. 1, the particular bis-phenoxy compound (and the antimony trioxide enhancing agent where indicated) is incorporated into the plastic (which is dried to remove moisture therefrom) by adding both to a Waring blender which contains acetone as a dispersing liquid. The resultant mixture, after blending for 3 minutes, is poured into evaporation dishes and the acetone evaporated, first at room temperature (20°-25° C.) for 60 minutes and followed by oven drying at 60° C. for one hour.

The percentages by weight of each component utilized in the respective formulations are listed in Table III. Each formulation is discharged from the evaporation dish and is ground into powder. The powder is subjected to compression molding in a Wabash press by placing said powder between two platens, the bottom of which contains four equal size depressions three inches by five inches by 1/8 inch deep. The top platen is then placed over the bottom platen and heat transfer means supplied thereto in order to melt said powder and thus provide solid samples (after cooling) for testing. The temperature and ram pressure utilized are respectively 100° C. and 30 tons.

A polypropylene plastic material, (Hercules Pro-fax® 6523 grade of polypropylene) is utilized as the base resin in order to prepare 13 formulations (plastic compositions) -- Nos. 11-23 shown in Table III. With the exception of formulation No. 11, the particular bis-phenoxy compound (and the antimony trioxide enhancing agent where indicated) is incorporated into the plastic and solid samples prepared according to the procedure set forth in Example I.

A virgin nylon 6 plastic material, (Zytel® 211, a product of E. I du Pont de Nemours and Co., Wilmington, Delaware) is utilized as the base resin in order to prepare 7 formulations (plastic compositions) -- Nos. 24-30 shown in Table III. With the exception of formulation No. 24, the particular bis-phenoxy compound (and the antimony trioxide enhancing agent where indicated) is incorporated into the plastic and solid samples prepared according to the procedure set forth in Example I.

Regarding Formulation Nos. 31-33 in Table III, a virgin polymethylmethacrylate plastic material, Plexiglass® V (811) a commercially available product of Rohm and Haas Company, Philadelphia, Pennsylvania and being substantially free of additives, is utilized as the base resin in order to prepare 3 formulations (plastic compositions). With the exception of formulation No. 31, the particular bis-phenoxy compound (and the antimony trioxide enhancing agent where indicated) is incorporated into the plastic and solid samples prepared according to the procedure set forth in Example I.

Referring to Formulation Nos. 34-37 in Table III, an acrylonitrile-butadiene-styrene (ABS) polymer plastic material, Marbon TP-2098, a product of Marbon Division, Borg-Warner Corporation, Washington, West Virginia, and which is a slight process variation of their commercially available "T" grade ABS polymer, is utilized as the base resin in order to prepare four (4) formulations (plastic compositions). These formulations, Nos. 34-37, are prepared in accordance with the procedure described in ASTM D-1897-68.

Portions of the samples of each respective formulation (Nos. 1-37, Table III) prepared respectively according to the above described procedures are then subjected to two different standard flammability tests, i.e. UL 94 and ASTM D--2863-70, i.e. Oxygen Index, O.I.

The results of these flammability tests are shown in Table III.

                  TABLE III                                                        ______________________________________                                         FLAMMABILITY DATA FOR                                                          DIFFERENT PLASTIC COMPOSITIONS                                                 CONTAINING BIS-PHENOXY COMPOUNDS WITH AND                                      WITHOUT ENHANCING AGENTS                                                       FORMU- BIS-PHENOXY ENHANCING  OXYGEN                                           LATION COMPOUND    AGENT      INDEX   UL 94                                    NO.    FORMULA %   Sb.sub.2 O.sub.3, %                                                                       %       VALUE                                    ______________________________________                                         Polyacrylonitrile Polymer                                                      1.     --     0        0        22.5    SB                                     2.     III    2        0        23.5    SB                                     3.     III    5        0        23.8    SB                                     4.     III    10       0        24.0    SB                                     5.     III    5        5        25.3    SB                                     6.     III    5        10       25.3    SB                                     7.     II     2        0        23.0    SB                                     8.     II     5        0        23.0    SB                                     9.     II     10       0        24.0    SB                                     10.    II     5        5        25.0    SB                                     Polypropylene Polymer                                                          11.    --     0        0        18.0    Burns                                  12.    III    15       0        20.0    SB                                     13.    III    15       5        22.8    SB                                     14.    III    20       5        26.0    SB                                     15.    III    25       0        24.0    SB                                     16.    III    25       5        26.0    SB                                     17.    II     15       0        19.0    SB                                     18.    II     15       5        22.0    SB                                     19.    II     20       5        25.0    SB                                     20.    II     25       0        23.0    SB                                     21.    II     25       5        25.0    SB                                     22.    III    20       10       25.0    SB                                     23.    II     20       10       24.0    SB                                     ______________________________________                                         FLAMMABILITY DATA FOR                                                          DIFFERENT PLASTIC COMPOSITIONS                                                 CONTAINING "OTHER BIS-PHENOXY COMPOUNDS"                                       WITH AND WITHOUT ENHANCING AGENTS                                                     "OTHER                                                                  FORMU- BIS-PHENOXY ENHANCING  OXYGEN                                           LATION COMPOUNDS"  AGENT      INDEX   UL 94                                    NO.    FORMULA %   Sb.sub.2 O.sub.3, %                                                                       %       VALUE                                    ______________________________________                                         Nylon                                                                          24.    --     0        0        23.0    SB                                     25.    III    10       0        23.5    SB                                     26.    III    10       3        24.5    SB                                     27.    III    13       3        27.5    SE-2                                   28.    II     10       0        23.5    SB                                     29.    II     10       3        24.0    SB                                     30.    II     13       3        27.0    SE-2                                   Polymethylmethacrylate Polymer                                                 31.    --     0        0        18.0    SB                                     32.    II     15       0        20.5    SB                                     33.    II     15       5        20.5    SB                                     Acrylonitrile-Butadiene-Styrene (ABS) Polymer                                  34.    --     0        0        19.0    HB(SB)                                 35.    II     15       0        27.0    HB(SB)                                 36.    II     15       5        32.5    V-0(SE-0)                              37.    III    15       5        35.0    V-0(SE-0)                              ______________________________________                                    

Referring to Table III, the bis-phenoxy compound formula II or III relates to the structural formulae heretofor set forth; and the UL 94 values are on a graduated scale wherein the highest degree to lowest degree of flame retardancy is respectively SE-0 (V-0), SE-1 (V-1), SE-2 (V-2), SB (HB) and Burns.

The results shown in Table III demonstrate the unexpected and completely unpredictable results using different polymer systems, in this instance the unique effectiveness of the plastic composition containing a three component system which consists of the bis-phenoxy compounds, an enhancing agent and acrylonitrile-butadiene-styrene (ABS) polymer as compared to the use of such bis-phenoxy compound with or without an enhancing agent in a polyacrylonitrile polymer, a polymethylmethacrylate polymer, a nylon polymer and a polyolefin such as polypropylene polymer, the latter four of which polymers show substantially no increase in flame retardancy via the use of said bis-phenoxy compounds, with or without an enhancing agent.

Specifically referring to the polyacrylonitrile polymer compositions Nos. 1-10, formulation No. 1 (the control) has an UL value of SB. In Nos. 2-10, the use of the particular bis-phenoxy compound (with or without the enhancing agent) results, within experimental accuracy, in no increase in flame retardancy via incorporation of 2%, 5%, or 10% of the bis-phenoxy compound per se.

Regarding the use of an enhancing agent in formulation Nos. 5 and 6, the results obtained therefrom show that there is no increase in flame retardancy. Thus, for example No. 1 (control) has an UL value of SB and Nos. 5 and 6 (which have different enhancing agent levels, 5% versus 10%) have also an UL value of SB. In viewing the results of No. 3 (5%-0%) and No. 5 (5%-5%), it can be seen that even the use of the enhancing agent does not increase flame retardancy in a polyacrylonitrile polymer.

With reference to the polypropylene polymer compositions Nos. 11 thru 23, it can readily be seen from the UL 94 values that the incorporation of the particular bis-phenoxy compound therein resulted in substantially little, if any, increase in flame retardancy as compared to the control, considering the experimental accuracy. Even the use of an enhancing agent did not result in an increase in flame retardancy, note No. 12SB and No. 13-SB. Predicated upon this data, it is thus seen that the incorporation of the bis-phenoxy compounds (with or without an enhancing agent) in a polypropylene results in no flame retardant efficacy.

Specifically referring to the nylon polymer compositions Nos. 24-30, formulation No. 24 (the control) had an UL value of SB. In Nos. 25 and 28, the use of the particular bis-phenoxy compound results in no increase in flame retardancy via incorporation of 10% (SB versus SB) of the bis-phenoxy compound per se.

Regarding the use of an enhancing agent in formulation Nos. 26, 27, 29 and 30, the results obtained therefrom show there is substantially little, if any, increase in flame retardancy. Thus, for example, No. 1 (control) has an UL value of SB and Nos. 26 and 29 also have an UL value of SB. While Nos. 27 and 30 each have an UL value of SE-2, this is not considered a significant increase and thus even the use of the enhancing agent does not result in flame retardancy efficacy.

With reference to the polymethylmethacrylate polymer compositions Nos. 31, 32 and 33, it can readily be seen from the UL values, i.e. all SB, that the incorporation of the particular bis-phenoxy compound therein results in no increase in flame retardancy as compared to the control. Even the use of an enhancing agent did not result in an increase in flame retardancy. Consequently, it can readily be seen that the incorporation of the bis-phenoxy compounds in a polymethylmethacrylate results in no flame retardant efficacy.

The most unexpected results in flame retardancy were obtained via the incorporation of the particular bis-phenoxy compounds and enhancing agents in an acrylonitrile-butadiene-styrene (ABS) polymer. Referring specifically to formulation Nos. 34 and 37, the control, formulation No. 34, had an UL value of HB(SB). Notwithstanding the incorporation of 15% (No. 35) of the particular bis-phenoxy compound per se in the ABS polymer, there still results an UL value of SB. Use of the enhancing agent with both bis-phenoxy compounds formulae II and III, in formulation Nos. 36 and 37 results in an unexpected UL value change from SB (No. 35) to SE-0 (No. 36) and SE-0 (No. 37). In view of these results, it was quite unexpected that the ABS polymer system, having incorporated therein the particular bis-phenoxy compounds and enhancing agent would show such superior flame retardant efficacy based on the results obtained from the performance of the other four (4) polymers, i.e. polyacrylonitrile, polypropylene, nylon and polymethylmethacrylate polymer systems having the same bis-phenoxy compounds and enhancing agents incorporated therein. Consequently, it can readily be seen that it is not possible to predict the efficacy and/or functionality of any halogen-containing material (which may be suggested as a flame retardant) in any polymeric system until one actually conducts a substantial research program thereon and ascertains certain properties of the "flame retarded" system and its utility.

EXAMPLE VIII

Solid samples of eight different plastic compositions separately containing certain prior art compounds and the herein described bis-phenoxy compound, both with or without the herein described enhancing agents, are prepared according to the above described procedure of Example I, except that the specimens are injection molded instead rather than compression molded, and are subjected to the following tests in order to ascertain comparative properties of the resultant plastic compositions:

    ______________________________________                                         (1)  Flammability                                                                   (a) Oxygen Index, O.I.                                                                         :    ASTM Test No. D-2863-70                                   (b) UL-94       :    UL-94 Procedure described                                                      herein and dated February 1,                                                   1974.                                                (2)  Light Stability                                                                (Weather Ometer)                                                                               :    Procedure described herein                                (a) Visual rank      and in Example IV, except                                   (1 is the highest) that the light source is the                              (b) Gardner Colorimeter                                                                             Xenon arc rather than a                                     (" Δ E" Values)                                                                             carbon arc.                                          (3)  Initial Color   :    Visual color observation                                                       immediately after injection                                                    molding.                                             (4)  Visual Migration                                                                               :    Visual observation of sur-                                                     face haze presence.                                  (5)  TGA and Isotherm                                                                               :    Procedure described in                                                         Example V.                                           (6)  Melt Flow       :    ASTM Test No. 1238-70.                               (7)  Notched Izod Impact                                                                            :    ASTM Test D256-72a; and                              (8)  Heat Distortion                                                                Temperature (HDT)                                                                              :    ASTM Test No. D648-72.                               ______________________________________                                    

Regarding item (2) above, i.e. light stability, the results obtained via the "Visual" rank include any color changes which occurred in the molded materials tested from a combination of processing and exposure to the xenon arc.

Each of the aforementioned Tests are standard test in the art and are utilized collectively in order to ascertain the efficacy of a polymeric system as an overall flame retardant composition for commercial application. All of these tests are to be considered as incorporated herein by reference.

The different polymers utilized along with trade names and corresponding suppliers are listed below.

    ______________________________________                                         Polymer      Trademark        Supplier                                         ______________________________________                                         Polycarbonate                                                                              Lexan 141       General Electric                                   Polystyrene Bakelite TMDE-6500                                                                             Union Carbide                                       (high impact) HIPS                                                            ABS         Cycolac T-2098  Borg-Warner                                        Nylon 6     Zytel 211       DuPont                                             Polypropylene                                                                              Profax 6523     Hercules                                           Terephthalate                                                                  polyester   Valox 310       General Electric                                   Polyphenylene                                                                  oxide,      Noryl 731       General Electric                                    modified (PPO)                                                                Polyethylene,                                                                              Bakelite DPD-3900                                                                              Union Carbide                                       Low Density                                                                   (LDPE)                                                                         ______________________________________                                    

The concentration of the additives (i.e. prior art compounds --designated PAC--or certain bis-phenoxy compounds --designated BPC--with or without an enhancing agent --designated EA--and the respective Table Nos. listing the pertinent data are shown below. The Table numbers are shown in parenthesis.

    ______________________________________                                                   PAC or BPC/EA     PAC or                                             Polymer   Sb.sub.2 O.sub.3 %                                                                               BPC ONLY                                           ______________________________________                                         Polycarbonate                                                                           3/1 (IV)                                                              HIPS     12/4(V)          16/0(VI) + 30/0(VII)                                 ABS      15/5(VIII)       20/0(IX) + 30/0(X)                                   Nylon    12/4(XI)                                                              Polypropylene                                                                           12/4(XII)                                                             Polyester                                                                               12/4(XIII)       16/0(XIV)                                            PPO      9/3(XV)                                                               PPO      9/3 Pigmented TiO.sub.2 (XVI)                                         LDPE     20/5(XVII)                                                            ______________________________________                                    

All percentages (%) shown are on a weight basis, based on the total weight of the plastic composition.

The identification of the prior art compounds (PAC) listed as A, B, C, D, E and F in the Tables are shown below:

    ______________________________________                                         PAC (Letter)                                                                             FORMULA                                                              ______________________________________                                         A         C.sub.6 Cl.sub.5 C.sub.6 Cl.sub.5                                              Bis-(decachlorobiphenyl)                                             B         C.sub.6 Br.sub.5 OC.sub.6 Br.sub.5                                             Bis-(pentabromophenyl)ether                                          C         C.sub.6 Br.sub.6                                                               Hexabromobenzene                                                     D         C.sub.6 Br.sub.5 CH.sub.2 Br                                                   Pentabromobenzyl bromide                                             E         C.sub.6 H.sub.2 Br.sub.2 (OCH.sub.3)C(CH.sub.3).sub.2 C.sub.6                  H.sub.2 Br.sub.2 (OCH.sub.3)                                                   Bis-2,2-(3,5-dibromo-4-                                                        methoxyphenyl)propane                                                F         C.sub.6 H.sub.2 Br.sub.3 OCH.sub.2 CBr=CBrCH.sub.2 OC.sub.6                    H.sub.2 Br.sub.3                                                               Trans 1,4-Bis(2,4,6-tribromophenoxy)-                                          2,3-dibromo-2-butene                                                 ______________________________________                                    

The certain bis-phenoxy compounds (BPC) listed in the Tables under Present Invention, as II, III, VI, etc. correspond to those compounds listed on pages 11 and 12 of this specification.

The control (base resin) is the particular designated polymer without the PAC, BPC or EA.

The results of this comparative testing are set forth in Tables IV through XVII.

                                      Table IV                                     __________________________________________________________________________                  Control                                                                             Prior Art                Present Invention                   ResinPolycarbonate                                                                          (Base                                                                              Compounds                 Compounds                           Additive 3/1 Resin)                                                                             A    B   C   D   E   F    II   III IV                                                                               VI  VIII                                                                              IX                __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                            25.0                                                                               36.5 41.5                                                                               39.5                                                                               39.5                                                                               37.0     36.5 37.5  40.0                     UL-94 1/8" thickness                                                                        HB  V-2  V-0 V-2 V-2 V-0      V-0  V-0   V-0                      Xenon Arc                                                                      Weather-Ometer (Ranked)                                                                     1   5    10  8   9   3        2    4     7                        Injection Molded                                                                            Clear                                                                              Light                                                                               Light                                                                              Light                                                                              Cream                                                                              Light                                                                              Decom-                                                                              Off- Cream Off-                     Initial Color    Cream                                                                               Cream                                                                              Cream   Cream                                                                              positon                                                                             White      White                                     Perhaps                   Perhaps                             Initial          Slight                                                                              None                                                                               None                                                                               None                                                                               None                                                                               "    Slight                                                                              None  None                     Visual Migration                                                               7 days           None None                                                                               None                                                                               None                                                                               None     None None  None                     TGA 5% wt. Loss ° C.                                                                 427 381  379 375 366 378      398  374   388                      Isotherm 24 hr. 200° C.                                                              0.394                                                                              1.20 0.529                                                                              1.78                                                                               1.18                                                                               1.12     0.664                                                                               0.655 0.326                    Melt Flow g/10 min.                                                            Conditions 275° C.,                                                                  9.8 11.8 12.7                                                                               18.8                                                                               17.2                                                                               16.8     8.8  17.4  11.4                     1,200g                                                                         Notched Izod Impact                                                            ft. lbs/in. 1/2 × 1/8                                                                 16.50                                                                              6.64 8.54                                                                               2.73                                                                               1.02                                                                               3.16     16.98                                                                               7.25  9.41                     Heat Deflection Temp.                                                          ° F. at 264 psi,                                                                     279 265  267 260 259 262      265  259   268                      Annealed at 200° F.                                                     Concentrate Compounding               Degrad-                                  Temperature, ° F.                                                                        500  480 480 500 500 ed at                                                                               500  500   500                                                            500                                      Injection Molding                                                              Temperature, ° F.                                                                    520 520  520 520 520 520      520  520   520                      Gardner Color Value, Δ E                                                 After 48 hours,                                                                             1.1 4.7  22.2                                                                               10.1                                                                               6.7 3.8      3.6  3.6   9.6                      Xenon Arc                                                                      __________________________________________________________________________

                                      Table V                                      __________________________________________________________________________                Control                                                                             Prior Art              Present Invention                       ResinABS   (Base                                                                              Compounds               Compounds                               Additive 15/5                                                                             Resin)                                                                             A   B   C   D   E   F   II  III VI  IV  VIII                                                                               IX                  __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                          18.5                                                                               21.5                                                                               28.0                                                                               27.5                                                                               35.0                                                                               26.0                                                                               34.5                                                                               30.5                                                                               28.0                                                                               30.5                                                                               31.0                                                                               36.0                                                                               30.0                UL-94 1/8" HB  HB  V-0 V-0 V-0 HB  V-0 V-0 V-0 V-0 V-0 V-0 V-0                 thickness                                                                      Xenon Arc                                                                      Weather-Ometer                                                                            5   6   12  10  13  3   11  7   8   9   2   1   4                   (Ranked)                                                                       Injection Molded                                                               Initial Color                                                                             White                                                                              Off-                                                                               Off-                                                                               Off-                                                                               Tan Off-                                                                               Light                                                                              White                                                                              White                                                                              White                                                                              White                                                                              White                                                                              White                              White                                                                              White                                                                              White   White                                                                              Cream                                       Visual  Initial                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                            Migration7 days                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                                                                               None                                           266     249                                                     TGA 5% wt. loss °C.                                                                329 48 hr                                                                              307 48 hr                                                                              261 271 274 285 290 310                             Isotherm 72 hr.,                                                                          1.83                                                                               0.415   0.727       1.27                                                                               1.11                                    150° C.                                                                 Melt Flow g/10 min.                                                            Conditions "G"                                                                            3.2 3.6 4.0 4.5 8.3 9.9 4.9 8.2 6.7 3.4                             200° C., 5,000g                                                         Notched Izod Impact                                                            ft. lbs/in.                                                                               3.27                                                                               1.62                                                                               1.40                                                                               1.19                                                                               1.56                                                                               1.62                                                                               1.23                                                                               1.93                                                                               2.12                                                                               1.19                                                                               2.08                                                                               1.92                                                                               1.32                1/8 × 1/8                                                                Heat                                                                           Deflection Temp.                                                               ° F. at 264 psi                                                                    192 189 187 190 184 171 185 180 176 190                             Annealed at 180° F.                                                     Concentrate                                                                    Compounding    400 400 400 400 400 400 450 350 400 400 400 400                 Temperature, °F.                                                        Injection Molding                                                              Temperature, ° F.                                                                  450 450 450 450 450 450 430 450 450 450 450 450 450                 Gardner                                                                        Color Value, Δ E                                                         After 100 hours,                                                                          6.5 3.9 20.1                                                                               11.9                                                                               12.7                                                                               4.6 8.6 6.7 7.9 7.3 0.9 4.1 1.1                 Xenon Arc                                                                      __________________________________________________________________________

                                      Table VI                                     __________________________________________________________________________                   Control                                                                             Prior Art               Present Invention                   ResinABS      (Base                                                                              Compounds                Compounds                           Additive 20/0 Resin)                                                                             A   B   C   D   E   F    II  III IV                                                                               VI  VIII                                                                              IX                 __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                             18.5                                                                               20.5                                                                               24.5                                                                               24.0                                                                               27.0                                                                               22.5     24.0                                                                               22.5  27.0                      UL-94 1/8" thickness                                                                         HB  HB  HB  V-0 V-0 HB       HB  HB    V-0                       Xenon Arc                                                                      Weather-Ometer (Ranked)                                                                      1   5   7   6   8   1        2   3     4                         Injection Molded                                                                             White                                                                              Off-                                                                               Off-                                                                               Off-                                                                               Tan White                                                                              Decom-                                                                              White                                                                              White Off-                      Initial Color     White                                                                              White                                                                              White       posed          White                     Initial                                                                        Visual Migration  None                                                                               None                                                                               None                                                                               None                                                                               None                                                                               "    None                                                                               None  None                      7 days                                                                         TGA 5% wt. loss ° C.                                                    Isotherm 72 hr., 150° C.                                                Melt Flow g/10 min.                                                            Conditions "G" 200° C.,                                                 5,000g                                                                         Notched Izod Impact                                                            ft.lbs/in. 1/2 × 1/8                                                                   3.27                                                                               1.40                                                                               1.43                                                                               1.17                                                                               1.15                                                                               1.97     3.27                                                                               4.18  1.45                      Heat Deflection Temp.                                                          °F. at 264 psi,                                                         Annealed at 180° F.                                                     Concentrate Compounding                                                        Temperature, ° F                                                                          400 400 400 400 400 400  400 400   400                       Injection Molding                                                              Temperature, ° F                                                                      450 450 450 450 420 450      450 450   450                       Gardner Color Value, Δ E                                                 After 100 hours,                                                                             6.5 8.0 19.8                                                                               11.1                                                                               8.5 4.6 --   4.4 5.2   5.6                       Xenon Arc                                                                      __________________________________________________________________________

                                      Table VII                                    __________________________________________________________________________                  Control                                                                             Prior Art              Present Invention                     ResinABS     (Base                                                                              Compounds               Compounds                             Additive 30/0                                                                               Resin)                                                                             A   B   C   D   E   F   II  III IV VI  VIII                                                                               IX                 __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                            18.5                                                                               21.5                                                                               30.0                                                                               30.0                                                                               32.0                                                                               27.0                                                                               30.0                                                                               33.5                                                                               34.0   35.5                       UL-94 1/8" thickness                                                                        HB  HB  V-0 V-0 V-0 V-0 V-0 V-0 V-0    V-0                        Xenon Arc                                                                      Weather-Ometer (Ranked                                                                      3   5   10  8   11  1   7   4   2      6                                           Egg Egg Egg                        Egg                        Injection Molded                                                                            White                                                                              Shell                                                                              Shell                                                                              Shell                                                                              Light                                                                              White                                                                              Light                                                                              White                                                                              White  Shell                      Initial Color    White                                                                              White                                                                              White                                                                              Brown   Tan            White                      Initial                                                                        Visual Migration                                                               7 days                                                                         TGA 5% wt. loss °C.                                                     Isotherm 72 hr., 150° C.                                                Melt Flow g/10 min.                                                            Conditions "G" 200° C.,                                                 5,000g                                                                         Notched Izod Impact                                                            ft. lbs/in. 1/2  × 1/8                                                                3.27                                                                               1.06                                                                               1.08                                                                               1.09                                                                               1.50                                                                               1.42                                                                               1.19                                                                               2.49                                                                               3.65   1.13                       Heat Deflection Temp.                                                          ° F. at 264 psi,                                                        Annealed at 180° F.                                                     Concentrate Compounding                                                                     --  440 440 440 392 392 356 440 400    440                        Temperature, ° F.                                                       Injection Molding                                                              Temperature, ° F.                                                                    450 450 450 450 400 430 400 450 450    450                        Gardner Color Value, Δ E                                                              6.5 1.4 9.0 2.6 6.5 1.6 2.5 2.6 1.2    0.8                        After 100 hours,                                                               Xenon Arc                                                                      __________________________________________________________________________

                                      Table VIII                                   __________________________________________________________________________               Control                                                                             Prior Art                 Present Invention                     ResinHips (Base                                                                              Compounds                  Compounds                             Additive 12/4                                                                            Resin)                                                                             A   B    C    D   E    F   II  III IV                                                                               VI  VIII                                                                               IX                  __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                         18.5                                                                               20.0                                                                               26.0 23.5 27.0                                                                               23.0 25.0                                                                               21.0                                                                               23.0  25.5                                                                               26.5                                                                               26.0                UL-94 1/8"                                                                               HB  HB  V-0  V-0  V-0 HB   V-2 HB  HB    V-0 V-0 HB                  thickness                                                                      Xenon Arc                                                                      Weather-Ometer                                                                           1   5   11   10   12  3    9   4   6     8   2   7                   (Ranked)                                                                       Injection Molded                                                                         White                                                                              Light                                                                              Cream                                                                               Grey Light                                                                              White                                                                               Tan Off-                                                                               Off-  Off-                                                                               Off-                                                                               Off-                Initial Color Cream    Cream                                                                               Cream        White                                                                              White White                                                                              White                                                                              White                ##STR15##                                                                                None None                                                                          None None                                                                          ##STR16##                                                                           ##STR17##                                                                           None  None                                                                         Perhaps Slight None                                                                 None None                                                                          None None                                                                          None None                                                                            None None                  TGA 5% wt. loss ° C.                                                              322 270 325  263  254 279  277 304 305   325                         Isotherm 48 hr.,                                                                         0.582                                                                150° C.                                                                           0.410                                                                              1.44                                                                               0.301                                                                               1.04 3.12                                                                               1.17 0.885                                                                              0.940                                                                              0.758 0.22                        Melt Flow g/10 min.                                                            Conditions "G"                                                                           6.2 11.0                                                                               8.8  10.4 13.3                                                                               11.1 15.8                                                                               10.7                                                                               13.8  7.1                         200° C.,                                                                          5,000g                                                               Notched Izod Impact                                                            ft.lbs/in.                                                                               2.12                                                                               1.61                                                                               1.71 1.66 1.65                                                                               1.64 1.25                                                                               1.76                                                                               1.63  1.69                                                                               1.73                                                                               1.72                1/2 × 1/8                                                                Heat                                                                           Deflection Temp.                                                               ° F. at 264 psi,                                                                  182 171 180  171  165 157  172 172 157   177                         Annealed at 160° F.                                                     Concentrate                                                                    Compounding                                                                              --  400 400  400  400 400  400 450 400   400 400 400                 Temperature, ° F.                                                       Injection Molding                                                                        450 450 450  450  450 430  430 450 430   450 450 450                 Temperature, ° F.                                                       Gardner                                                                        Color Value, ΔE                                                          After 24 hours,                                                                          0.7 17.6                                                                               33.6 23.9 34.3                                                                               7.0  11.0                                                                               11.0                                                                               20.9  14.4                                                                               4.3 16.3                Xenon Arc                                                                      __________________________________________________________________________

                                      Table IX                                     __________________________________________________________________________                   Control                                                                             Prior Art                Present Invention                  ResinHIPS     (Base                                                                              Compounds                 Compounds                          Additive 16/0 Resin)                                                                             A   B   C   D    E   F    II  III IV                                                                               VI  VIII                                                                              IX                __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                             18.5                                                                               18.5                                                                               22.0                                                                               22.0     21.5     21.0                                                                               21.5  22.0                     UL-94 1/8" thickness                                                                         HB  HB  V-2 HB       HB       HB  HB    HB                       Xenon Arc                                                                      Weather-Ometer (Ranked)                                                                      1   2   9   7        5        3   6     4                        Injection Molded                                                                             White                                                                              Off-                                                                               Cream                                                                              Cream                                                                              Decom-                                                                              White                                                                              Decom-                                                                              Off-                                                                               White Cream                    Initial Color     White       posi-    posi-                                                                               White                                                            tion     tion                                     ##STR18##         None None                                                                          None None                                                                          None None                                                                               None  None                                                                              None None                                                                          None None                                                                            None None               TGA 5% wt. loss ° C.                                                    Isotherm 72 hr. 150° C.                                                 Melt Flow g/10 min.                                                            Conditions "G" 200° C                                                   5,000g                                                                         Notched Izod Impact                                                            ft lbs/in. 12 × 1/8                                                                    2.12                                                                               1.64                                                                               1.69                                                                               1.58     1.59     1.62                                                                               1.60  1.66                     Heat Deflection Temp.                                                          ° F. at 264 psi,                                                        Annealed at 180° F.                                                     Concentrate Compounding                                                        Temperature, ° F.                                                                         400 400 400      400      400 400   400                      Injection Molding                                                                            450 450 450 450      450      450 450   450                      Temperature, ° F.                                                       Gardner Color Value, Δ E                                                 After 24 hours, Xenon Arc                                                                    0.7 19.4                                                                               25.9                                                                               23.2     21.7     34.0                                                                               30.5  17.8                     __________________________________________________________________________

                                      Table X                                      __________________________________________________________________________                   Control                                                                              Prior Art             Present Invention                    ResinHIPS     (Base                                                                               Compounds              Compounds                            Additive 30/0 Resin)                                                                              A   B   C  D   E   F   II  III IV VI  VIII                                                                              IX                 __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                             18.5 21.0                                                                               25.5                                                                               25.5                                                                              30.0                                                                               25.0                                                                               27.0                                                                               27.0                                                                               25.0   32.0                      UL-94 1/8" thickness                                                                         HB   HB  V-0 V-0                                                                               V-0 V-0 V-0 V-0 V-0    V-0                       Xenon Arc                                                                      Weather-Ometer (Ranked)                                                                      1    5   10  7  9   2   8   4   6      3                         Injection Molded                                                                             Trans-                                                                              Beige                                                                              Light                                                                              Grey                                                                              Brown                                                                              Light                                                                              Tan Off-                                                                               Off-   Light                     Initial Color luscent  Grey       Tan     White                                                                              White  Biege                      ##STR19##                                                                     TGA 5% wt. loss ° C.                                                    Isotherm 72 hr., 150° C.                                                Melt Flow g/10 min.                                                            Conditions "G" 200° C.,                                                 5,000g                                                                         Notched Izod Impact                                                            ft.lbs/in. 1/2 × 1/8                                                                   2.12 1.10                                                                               1.21                                                                               1.43                                                                              1.45                                                                               1.27                                                                               1.11                                                                               1.39                                                                               1.35   R 1.08                                                                         1.10                      Heat Deflection Temp.                                                          ° F. at 264 psi,                                                        Annealed at 180° F.                                                     Concentrate Compounding                                                        Temperature, ° F.                                                                          450 450 430                                                                               356 392 356 450 400    450                       Injection Molding                                                              Temperature, °F.                                                                      450  430 430 410                                                                               380 400 380 430 410    430                       Gardner Color Value, Δ E                                                 After 24 hours, Xenon Arc                                                                    0.7  22.4                                                                               29.7                                                                               15.8                                                                              10.4                                                                               5.1 12.1                                                                               17.2                                                                               24.9   6.8                       __________________________________________________________________________

                                      Table XI                                     __________________________________________________________________________                   Control                                                                             Prior Art              Present Invention                    ResinNylon 6  (Base                                                                              Compounds               Compounds                            Additive 12/4 Resin)                                                                             A   B   C   D   E   F   II  III  IV VI  VIII                                                                              IX                __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                             21.5                                                                               26.0                                                                               28.5                                                                               29.0            24.5        27.5                     UL-94 1/8" thickness                                                                         HB  V-2 V-0 V-2 Did De- Did-                                                                               V-2 Molding V-0                                                                    Pro-                             Xenon Arc                                     blems                            Weather-Ometer (Ranked)       Not com-                                                                               Not     Decom-                           Injecton Molded                                                                              Natural                     Off-                                                                               posed                            Initial Color (white)                                                                            Cream                                                                              Cream                                                                              Cream                                                                              Mold                                                                               posed                                                                              Mold                                                                               White       Cream                     ##STR20##         None None                                                                          None None                                                                          None None       None None   None None               TGA 5% wt. loss ° C.                                                                  237 219 219 204             214         220                      Isotherm 48 hr. 150° C.                                                               5.67                                                                               4.70                                                                               4.60                                                                               4.76            4.49        4.97                     Melt Flow g/10 min.                                                            Conditions "G" 100° C.                                                  5000g                                                                          Notched Izod Impact                                                            ft.lbs/in. 1/2 × 1/8                                                                   3.09                                                                               1.85                                                                               1.66                                                                               1.60            2.54        2.20                     Heat Deflection Temp.                                                          ° F. at 264 psi,                                                                      125 137 133 135             132         136                      Annealed at 100° F.                                                     Concentrate Compounding                                                        Temperature, ° F.                                                                         440 440 440     440     440         440                      Injection Molding                                                              Temperature, ° F.                                                                     480 480 480 480     450     480         480                      Gardner Color Value, Δ E                                                 After 100 hours, Xenon                                                                       0.9 2.0 3.7 2.5             2.4         7.9                      Arc                                                                            __________________________________________________________________________

                                      Table XII                                    __________________________________________________________________________                Control                                                                            Prior Art                  Present Invention                    Resin Polypropylene                                                                       (Base                                                                              Compounds                  Compounds                            Additive 12/4                                                                             Resin)                                                                             A    B    C   D   E    F   II   III  IV                                                                               VI  VIII                                                                              IX                __________________________________________________________________________     Oxygen Index, %                                                                at 73° F                                                                           17.5                                                                               21.0 24.0 25.0                                                                               24.0                                                                               20.5 31.5                                                                               21.5 23.5   23.0                     UL-94 1/8" thickness                                                                      HB  HB   V-2  HB  V-2 HB   V-O HB   V-2    HB                       Xenon Arc                                                                      Weather-Ometer                                                                            1   4    11   9   10  5    8   3    2      6                        (Ranked)                                                                       Injection Molded                                                                          Clear                                                                              Off- Off- Cream                                                                              Cream                                                                              Off- Cream                                                                              Off- Off-   Off-                     Initial Color  White                                                                               White        White    White                                                                               White  White                     ##STR21##     Perhaps Slight Perhaps Slight                                                        Perhaps Slight None                                                                 None None                                                                          None None                                                                         Perhaps  Slight None                                                                    Perhaps Slight Perhaps Slight                                                       Perhaps Slight Perhaps                                                         Slight  None None                          272 264  274  256 252 260  269 275  273    276                      TGA 5% wt. loss ° C.                                                               0.00                                                                Isotherm 48 hr. 150° C.                                                            0.20                                                                               0.937                                                                               0.493                                                                               3.7 13.6                                                                               2.14 0.756                                                                              0.607                                                                               0.873  0.33                     Melt Flow g/10 min.                                                                       5.2 9.3  6.8  9.8 9.3 9.9  17.7                                                                               10.4 8.9    6.4                      Conditions "L", 230° C.                                                 2,160g                                                                         Notched Izod Impact                                                                       1.22                                                                               1.19 1.21 1.12                                                                               1.16                                                                               1.13 1.10                                                                               0.96 1.07   1.20                     ft.lbs/in. 1/2 × 1/8                                                     Heat Deflection Temp.                                                           ° F. at 66 psi,                                                                   246 253  240  276 240 235  267 267  257    277                       Annealed at 194° F.                                                    Concentrate Com-                                                                              400  420  400 360 450  420 400  400    400                      pounding Tempera-                                                              ture, ° F.                                                              Injection Molding                                                                         440 440  440  440 440 440  400 440  440    440                      Temperature, °F. -Gardner Color Value,                                             0.5 5.3  12.8 10.0                                                                               8.8 5.6  7.3 2.7  2.7    4.8                      Δ E After 48 hours,                                                      Xenon Arc                                                                      __________________________________________________________________________

                                      Table XIII                                   __________________________________________________________________________                    Control                                                                            Prior Art                Present Invention                  Resin Polyester                                                                               (Base                                                                              Compounds                Compounds                          Additive 12/4  Resin)                                                                             A   B   C   D   E   F    II  III IV                                                                               VI  VIII                                                                              IX                __________________________________________________________________________     Oxygen Index, %                                                                               22.0                                                                               28.0                                                                               32.0                                                                               32.0                                                                               32.0                                                                               26.0     30.0                                                                               29.0  32.0                     at 73° F                                                                UL-94 1/8" thickness                                                                          HB  V-2 V-0 V-0 V-0 V-2      V-2 V-2   V-0                      Xenon Arc                                                                      Weather-Ometer (Ranked)                                                                       1   5   9   7   8            3   2     4                        Injection Molded                                                                              White                                                                              Off-                                                                               Off-                                                                               Off-                                                                               Cream                                                                              Cream    White                                                                              White Cream                    Initial Color      White                                                                              White                                                                              White                                                ##STR22##         None None                                                                          None None                                                                          None None                                                                          None None                                                                          None None                                                                          Decomp- isition                                                                     None None                                                                          None None                                                                            None None                               369 281 346 266 292 305      311 330   351                      TGA 5% wt. loss ° C.                                                                   0.576                                                                              1.97                                                                               0.115                                                                              3.66                                                                               4.67                                                                               2.89     1.99                                                                               0.606 0.446                    Isotherm 24 hr. 200° C.                                                                0.489                                                           Melt Flow g/10 min.                                                                           15.0                                                                               11.5                                                                               12.8                                                                               10.8                                                                               22.0                                                                               16.5     6.5 25.8  11.3                     Conditions "H", 230° C., 1,200g                                         Notched Izod Impact                                                                           1.51                                                                               1.04                                                                               1.00                                                                               1.07                                                                               0.96                                                                               1.12     1.19                                                                               1.33  0.90                     ft.lbs/in. 1/2 × 1/8                                                     Heat Deflection Temp.                                                                         123 122 127 127 121 123      117 122   139                      ° F. at 264 psi                                                         Annealed at 100° F.                                                     Concentrate Compounding                                                                           450 450 450 450 450      450 450   450                      Temperature, ° F.                                                       Injection Molding                                                                             470 460 460 460 470 470      460 470   460                      Temperature, ° F.                                                       Gardner Color Value, Δ E                                                                1.9 7.8 22.6                                                                               7.3 8.5 1.9      3.4 3.1   4.2                      After 24 hours, Xenon Arc                                                      __________________________________________________________________________

                                      Table XIV                                    __________________________________________________________________________                    Control                                                                            Prior Art      Present Invention                            Resin Polyester                                                                               (Base                                                                              Compounds      Compounds                                    Additive 16/0  Resin                                                                              A  B  C  D E F II  III                                                                              IV  VI  VIII                                                                              IX                          __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                              22.0                                                                               28.0                                                                              23.0                                                                              28.5     27.5                                                                               27.5  27.5                               UL-94 1/8" thickness                                                                          HB  V-2                                                                               V-2                                                                               V-2      V-2 V-2   V-2                                Xenon Arc                                                                      Weather-Ometer (Ranked)                                                        Injection Molded                                                               Initial Color  White                                                                              Off-                                                                              Light                                                                             Light    Off-                                                                               White White                                                 White                                                                             Tan                                                                               Grey     White                                         ##STR23##                                                                     TGA 5% wt. loss ° C.                                                    Isotherm 24 hr., 200° C.                                                Melt Flow g/10 min.                                                            Conditions "H", 230° C., 1,260 g                                        Notched Izod Impact                                                                           1.51                                                                               0.93                                                                              1.32                                                                              1.13     1.19                                                                               1.33  1.13                               ft. lbs/in. 1/2 × 1/8                                                    Heat Deflection Temp.                                                          ° F. at 264 psi,                                                        Annealed at 100° F.                                                     Concentrate Compounding                                                                           450                                                                               450                                                                               450      470 470   450                                Temperature, ° F.                                                       Injection Molding                                                                             470 460                                                                               460                                                                               460      460 460   460                                Temperature, ° F.                                                       Gardner Color Value, Δ E                                                 After 24 hours, Xenon Arc                                                      __________________________________________________________________________

                                      Table XV                                     __________________________________________________________________________                    Control                                                                            Prior Art                Present Invention                  Resin PPO      (Base                                                                              Compounds                4None                              Additive 9/3   Resin)                                                                             A   B   C   D   E    F   II  III IV                                                                               VI  VIII                                                                              IX                __________________________________________________________________________     Oxygen Index, %                                                                at 73° F.                                                                              26.5                                                                               25.0                                                                               30.0                                                                               28.0                                                                               31.0                                                                               27.0 30.0                                                                               27.5                                                                               29.0  27.0                     UL-94 1/8" thickness                                                                          V-1 V-1 V-0 V-0 V-0 V-0  V-0 V-0 V-0   V-0                      Xenon Arc                                                                      Weather-Ometer (Ranked)                                                        Injection Molded                                                               Initial Color  Brown                                                                              Brown                                                                              Brown                                                                              Brown                                                                              Brown                                                                              Brown                                                                               Brown                                                                              Brown                                                                              Brown Brown                     ##STR24##          None None                                                                          None None                                                                          None None                                                                          None None                                                                         Perhaps Slight None                                                                  None None                                                                          None None                                                                          None None                                                                            None None               TGA 5% wt. loss °  C.                                                                  281 249 294 244 243 262  261 277 276   279                      Isotherm 24 hr. 200° C.                                                                1.87                                                                               4.07                                                                               2.21                                                                               5.00                                                                               3.88                                                                               3.19 5.40                                                                               3.08                                                                               3.19  2.35                     Melt Flow g/10 min.                                                                           1.4 3.3 2.1 2.6     3.7      3.8 3.0   1.9                      Conditions                                                                     Notched Izod Impact                                                                           4.02                                                                               2.39                                                                               2.44                                                                               2.44                                                                               1.94                                                                               2.97 1.77                                                                               2.50                                                                               2.60  1.89                     ft. lbs/in. 1/2 × 1/8                                                    Heat Deflection Temp.                                                                         209 196 205 200 200 177  194 193 190   203                      ° F. at 264 psi,                                                        Annealed at 200° F.                                                     Concentrate Compounding                                                                           450 450 450 450 450  450 450 450   450                      Injection Molding                                                                             450 450 450 450 450 450  450 450 450                            Temperature, ° F.                                                       Gardner Color Value, Δ E                                                 After   hours, Xenon Arc                                                       __________________________________________________________________________

                                      Table XVI                                    __________________________________________________________________________     Resin PPO     Control                                                                            Prior Art          Present Invention                         Additive 9/3  (Base                                                                              Compounds          Compounds                                  (Pigmented)  Resin)                                                                             A B  C  D    E  F  II III                                                                               IV                                                                               VI VIII                                                                              IX                          __________________________________________________________________________     Oxygen Index, %                                                                              25.0  32.0                                                                              31.0 33.5                                                                              26.5                                                                              32.5                                                                              28.0                                                                              28.5 30.0                              at 73° F.                                                               UL-94 1/8" thickness                                                                         HB    V-0                                                                               V-0  V-0                                                                               V-0                                                                               V-0                                                                               V-0                                                                               V-0  V-0                               Xenon Arc                                                                      Weather-Ometer (Ranked)                                                                      1     9  6    8  1  7  3  2    4                                 Injection Molded                                                                             Light Light                                                                             Light   Light                                                                             Dark                                                                              Light                                                                             Light                                                                               Light                             Initial Color Tan   Tan                                                                               Tan  Tan                                                                               Tan                                                                               Tan                                                                               Tan                                                                               Tan  Tan                                ##STR25##    None None                                                                            None None                                                                         None None                                                                           None None                                                                         None None                                                                         None None                                                                         None None                                                                         None None                                                                           None None                         TGA 5% wt. loss ° C.                                                                  389   335                                                                               284  291                                                                               311                                                                               275                                                                               338                                                                               324  337                               Isotherm 24 hr. 200° C.                                                               0.299 0.420                                                                             0.893                                                                               0.865                                                                             0.587                                                                             1.02                                                                              0.556                                                                             0.272                                                                               0.476                             Melt Flow g/10 min.                                                            Conditions                                                                     Notched Izod Impact                                                                          3.24  2.14                                                                              2.00 1.19                                                                              2.02                                                                              1.40                                                                              2.16                                                                              2.18 1.82                              ft. lbs/in. 1/2 × 1/8                                                    Heat Deflection Temp.                                                                        246   233                                                                               226  227                                                                               210                                                                               221                                                                               210                                                                               207  237                               ° F. at 264 psi,                                                        Annealed at 200° F.                                                     Concentrate Compounding                                                                      450   450                                                                               450  450                                                                               450                                                                               450                                                                               450                                                                               450  450                               Temperature, ° F.                                                       Injection Molding                                                                            460   460                                                                               460  460                                                                               460                                                                               460                                                                               460                                                                               460  460                               Temperature, ° F.                                                       Gardner Color Value, Δ E                                                               3.6   13.3                                                                              9.2  9.0                                                                               5.9                                                                               14.8                                                                              5.3                                                                               4.9  6.9                               After 48 hours, Xenon Arc                                                      __________________________________________________________________________

                                      Table XVII                                   __________________________________________________________________________                      Control                                                                            Prior Art             Present Invention                   Resin LDPE       (Base                                                                              Compounds             Compounds                           Additive 20/5    Resin)                                                                             A B   C   D   E   F   II  III                                                                              IV  VI  VIII                                                                              IX                 __________________________________________________________________________     Oxygen Index, %  18.0  28.0                                                                               29.0                                                                               27.0                                                                               26.5                                                                               26.5                                                                               26.0                                                                               28.0  26.5   25.5               at 73° F.                                                               UL-94 1/8" thickness                                                                            HB    V-0 V-2 V-2 V-2 V-2 V-2 V-0   V-0    V-2                Xenon Arc                                                                      Weather-Ometer (Ranked)                                                        Injection Molded Natural                                                                              Off-                                                                               Light                                                                              Off-                                                                               White                                                                              Cream                                                                              White                                                                              White White                     Initial Color          White                                                                              Grey                                                                               White                                            ##STR26##             None None                                                                          Yes Yes                                                                            Yes Yes                                                                            None None                                                                          None Yes                                                                           None  None                                                                         Yes Yes                                                                              None None                 TGA 5% wt. loss ° C.                                                                     302   330 248 248 265 267 305 308   332                       Isotherm 48 hr. 150° C.                                                                  0     0   1.84                                                                               2.42                                                                               0.78                                                                               0.66                                                                               0.26                                                                               0.41  0.16                      Melt Flow g/10 min.                                                            Conditions "G" 200 C 5000g                                                     Notched Izod Impact                                                                             NB    NB  NB      NB  NB      NB    NB     NB                 ft. - lbs/in. 1/2 × 1/8                                                                   >6.6  >7.1                                                                               >7.9                                                                               3.31                                                                               > 7.3                                                                              >8.3                                                                               2.12                                                                               >8.8  >8.1                      Heat Deflection Temp.                                                          ° F. at 264 psi                                                         Annealed at 180° F.                                                     Concentrate Compounding                                                        Temperature, ° F.                                                                        400   400 400 400 400 400 450 400   400    400                Injection Molding                                                                               430   450-                                                                               410 410 410 410 410 410   430    410                Temperature, ° F.                                                                              410                                                     Gardner Color Value, Δ E                                                 After 100 hours, Xenon Arc                                                                      0.4   9.8 8.5 4.4 2.1 7.5 3.9 1.3   3.0    2.4                __________________________________________________________________________

Referring to Tables IV through XVII in general, it is readily apparent that the incorporation of additives in polymer systems is highly unpredictable. Even in the same polymer, "structurally related" prior art compounds and bis-phenoxy compounds produced completely different results. However, out of all the data shown therein, it is clear that the combination of the bis-phenoxy compounds and enhancing agent result in an unexpected, superior, flame retarded polycarbonate composition which has commercial application.

Specifically, Table IV shows the results of testing a carbonate/BPC/EA combination is the only one (except composition E) which produced V-0(UL 94), Gardner color Δ E Values substantially the same as the control (without additives) and good thermal stability. In conjunction with composition E, it should be noted that the resultant composition exhibited very poor impact test results according to ASTM test D256-72a (Notched Izod Impact); consequently this compound is not suitable for commercial utility since it is important that those areas which utilize polycarbonates require and deem it critical to possess high impact values, which is one of the major reasons polycarbonates are selected for various end uses. Thus, composition E is not a suitable material because of the poor physical properties. Thus these PBC compounds, as a class, are unique. While B yielded a V-0(UL 94) composition, the Δ E Value was excessively high and thus non-applicable for commercial use. A, C and D show non-efficacy (V-2 ratings similar to the control) thereof as flame retardants and again point out the non-predictability of additives incorporated in either the same or various polymers. (The inclusion of data, relating to where no enhancing agent is used, is presented to show non-efficacy of BPC at low concentrations and the large quantities required to produce efficacy--note Tables VI and VII.)

In summary, the results shown in Tables IV through XVII are reviewed with the aforementioned criteria, i.e. UL-94 rating V-0, good light stability and thermal stability, and are presented in Table XVIII in terms of whether there is commercial utility, (taking into consideration all physical and mechanical properties) i.e. similar to those results shown for octabromobiphenyl in Modern Plastics Encyclopedia, idib. Table XVIII sets forth more vividly the difference between the present invention and the prior art and also the different results obtained when different polymers have the same additives incorporated therein; and also confirming those specific observations regarding the difference in polymer systems as noted by the Norris et al paper, ibid.

                                      TABLE XVIII                                  __________________________________________________________________________     FLAME RETARDANT EFFICACY OF DIFFERENT ADDITIVES IN DIFFERENT POLYMER           SYSTEMS                                                                        (IS THERE COMMERCIAL UTILITY BASED ON A POLYCARBONATE SYSTEM                   __________________________________________________________________________     CRITERIA?)                                                                                   Prior Art       Present Invention                                Polymers      Compounds + Enhancing Agents                                                                   Compounds + Enhancing Agents                     __________________________________________________________________________     I. Present Invention                                                                         A B  C D  E  F  II III                                                                               VI IV VIII                                                                              IX VII                            __________________________________________________________________________     Polycarbonate No                                                                               No No                                                                               No No No Yes                                                                               Yes                                                                               Yes                                        II. Comparative Polymers                                                       Polystyrene (HIPS)                                                                           No                                                                               No No                                                                               No No No No No Yes      No Yes                            ABS           No                                                                               No No                                                                               No No Yes                                                                               Yes                                                                               Yes                                                                               Yes                                                                               Yes                                                                               Yes                                                                               Yes                               Nylon         No                                                                               Yes                                                                               No   No    No No Yes                                        Polypropylene No                                                                               No No                                                                               No No Yes                                                                               No No No                                         Polyester     No                                                                               No ?*                                                                               ?* Yes                                                                               No No No Yes                                        Polyphenylene oxide (PPO)                                                                      ?* ?*                                                                               ?* Yes                                                                               ?* Yes                                                                               Yes                                                                               Yes                                        Polyethylene (LDPE)                                                                            ?* No                                                                               No No No No Yes                                                                               Yes                                        Polyacrylonitrile             No No                                            Polymethylmethacrylate        No No                                            __________________________________________________________________________      (*Perhaps Δ E Values Very High                                     

EXAMPLE IX

The procedure of Examples VII and VIII are repeated except that the enhancing agent used is zinc borate instead of antimony oxide. Substantially the same results are obtained using zinc borate as those using antimony oxide.

EXAMPLE X

The bis-phenoxy compounds described herein are subjected to toxicity tests and it is found that these compounds are not toxic orally, not irritating to the eye and not irritating to the skin, all as measured by the guidelines of the Federal Hazardous Substances Act. Furthermore, rat feeding studies indicate these materials are not biologically persistent, an important property to minimize ecological imbalance.

In view of the foregoing Examples and remarks, it is seen that the plastic compositions, which incorporate a three component system (including the bis-phenoxy compounds), possess characteristics which have been unobtainable in the prior art. Thus, the use of bis-phenoxy compounds and enhancing agents in polycarbonates as flame retardants therefor is quite unique since it is not possible to predict the effectiveness and functionality of any particular material in any polymer system until it has actively undergone incorporation therein and the resultant plastic composition evaluated according to certain criteria such as UL 94 and various ASTM Standards. Further more, it is necessary, in order to have commercial utility, that the resultant flame retarded plastic composition possess characteristics such as being non-toxic and not biologically persistent. Use of the bis-phenoxy compounds and an enhancing agent in polycarbonates has accomplished all of these objectives.

Thus, in order to meet the needs and standards of commerce, it is necessary that a successful candidate fulfill all of the requirements outlined above, not just a selected group. It was totally unexpected that this specific group of bisphenoxy compounds meet these requirements in all aspects contrary to the expectations of the suggested teachings of the prior art.

The above examples have been described in the foregoing specification for the purpose of illustration and not limitation. Many other modifications and ramifications will naturally suggest themselves to those skilled in the art based on this disclosure. These are intended to be comprehended as within the scope of this invention. 

What is claimed is:
 1. A plastic composition comprising a three component system consisting of (1) a polycarbonate, (2) a bis-phenoxy compound, which functions as a flame retardant for said composition, having the formula ##STR27## wherein (a) Z is bromine; (b) m and m' are independent and are integers having a value of from 1 to 5 with the proviso that the bromine atom content is from 6 to 10 bromine atoms; and (c) T is a straight or branched chain carbon group having from one to four carbon atoms, and (3) a flame retardant enhancing agent.
 2. The composition as set forth in claim 1 wherein the amount of said bis-phenoxy compound employed is from about 1% to about 25% by weight, based on the total weight of said composition.
 3. The composition as set forth in claim 2 wherein the T is CH₂.
 4. The composition as set forth in claim 2 wherein the T is (CH₂)₂.
 5. The composition as set forth in claim 2 wherein the T is (CH₂)₃.
 6. The composition as set forth in claim 2 wherein the T is (CH₂)₄.
 7. The composition as set forth in claim 2 wherein the T is ##STR28##
 8. The composition as set forth in claim 2 wherein the T is ##STR29##
 9. The composition as set forth in claim 2 wherein the enhancing agent is selected from the group consisting of oxides and halides of Groups IV A and V A of the Periodic Table of Elements.
 10. The composition as set forth in claim 9 wherein the T is (CH₂)₂ and m and m' are each
 5. 11. The composition as set forth in claim 9 wherein the T is (CH₂)₂ and m and m' are each
 3. 12. The composition as set forth in claim 9 wherein the T is (CH₂)₃ and m and m' are each
 3. 13. The composition as set forth in claim 9 wherein the T is (CH₂)₄ and m and m' are each
 3. 14. The composition as set forth in claim 9 wherein the T is CH₂ and m and m' are each
 3. 15. The composition as set forth in claim 9 wherein the T is CH₂ and m and m' are each
 5. 16. The composition as set forth in claim 9 wherein the T is (CH₂)₂ and m is 5 and m' is
 3. 17. The composition as set forth in claim 9 wherein the enhancing agent is antimony oxide.
 18. A flame retarded, shaped plastic composition comprising a three component system which consists of (a) a polycarbonate, (b) a bis-phenoxy compound selected from the group consisting of (i) 1,2-bis(2,4,6-tribromophenoxy)ethane, (ii) 1,3,-bis(2,4,6-tribromophenoxy)propane and (iii) 1,2,-bis(2,3,4,5,6-pentabromophenoxy)ethane and (c) an enhancing agent selected from the group consisting of oxides of antimony, arsenic and bismuth; with the proviso that said plastic composition if further characterized by having a flammability rating of SE-0 (V-0) as determined by the UL 94 procedure described in the specification.
 19. A substantially white, flame retarded, injection molded plastic composition comprising a three component system which consists of (a) a polycarbonate, (b) a bis-phenoxy compound selected from the group consisting of (i) 1,2-bis(2,4,6-tribromophenoxy)ethane, (ii) 1,2-bis(2,4,6-tribromophenoxy)-propane, and (c) an enhancing agent selected from the group consisting of oxides of antimony, arsenic and bismuth; with the proviso that said plastic composition is further characterized by having a flammability rating of SE-0 (V-0) as determined by the UL-94 procedure described in the specification and an Δ E Color Value of less than
 10. 20. The composition as set forth in claim 19 wherein (a) the bis-phenoxy compound is 1,2-bis(2,4,6-tribromophenoxy) ethane and is present in an amount of from about 1% by weight to about 10% by weight, based on the total weight of said composition and (b) the enhancing agent is antimony trioxide and is present in an amount of from about 1% by weight to about 10% by weight, based on the total weight of said composition.
 21. A composition as set forth in claim 20 wherein the amount of said bis-phenoxy compound is about 5% by weight, based on the total weight of said composition, and said enhancing agent is present in an amount of about 3% by weight, based on the total weight of said composition.
 22. A composition as set forth in claim 20 wherein the amount of said bis-phenoxy compound is about 3% by weight, based on the total weight of said composition, and said enhancing agent is present in an amount of about 1% by weight, based on the total weight of said composition.
 23. A composition as set forth in claim 20 wherein said compound has a Notched Izod Impact of about 16.98 ft.lb/in. as determined by ASTM Test Number D256-72a and a heat distortion temperature of about 265° F. as determined by ASTM Test Number D648-72.
 24. The composition as set forth in claim 19 wherein (a) the bis-phenoxy compound is 1,3-bis(2,4,6-tribromophenoxy) propane and is present in an amount of from about 1% by weight to about 10% by weight, based on the total weight of said composition and (b) the enhancing agent is antimony trioxide and is present in an amount of from about 1% by weight to about 10% by weight, based on the total weight of said composition.
 25. A composition as set forth in claim 24 wherein the amount of said bis-phenoxy compound is about 2% by weight, based on the total weight of said composition, and said enhancing agent is present in an amount of about 2% by weight, based on the total weight of said composition.
 26. A composition as set forth in claim 24 wherein the amount of said bis-phenoxy compound is about 3% by weight, based on the total weight of said composition, and said enhancing agent is present in an amount of about 1% by weight, based on the total weight of said composition.
 27. A composition as set forth in claim 24 wherein said compound has a Notched Izod Impact of about 7.25 ft.lb/inc. as determined by ASTM Test Number D256-72a and a heat distortion temperature of about 259° F. as determined by ASTM Test Number D648-72.
 28. A composition as set forth in claim 19 wherein (a) the bis-phenoxy compound is 1,2-bis(2,3,4,5,6-pentabromophenoxy)ethane and is present in an amount of from about 1% by weight to about 20% by weight, based on the total weight of said composition and (b) the enhancing agent is antimony trioxide and is present in an amount of from about 1% by weight to about 10% by weight, based on the total weight of said composition.
 29. A composition as set forth in claim 28 wherein the bis-phenoxy compound is present in an amount of about 3% by weight, based on the total weight of said composition and the enhancing agent is present in an amount of about 1% by weight based on the total weight of said composition, and said composition has a Notched Izod Impact of about 9.41 ft.lbs/in. as determined by ASTM Test Number D256-72a and a heat distortion temperature of about 268° F. as determined by ASTM Test Number D648-72. 